Sintéis de mulite

Is féidir an modh sintéirithe mullite a roinnt ina mhodh shintéirithe agus modh leá leictreach. Is féidir modh shintéirithe a roinnt ina mhodh tirim agus modh fliuch de réir an mhodha ullmhúcháin amhábhar. Is é an próiseas tirim ná na comhábhair a mheilt le chéile agus ansin é a dhó trí áith rothlacha nó áith tolláin tar éis an liathróid a bhrú nó a dhlúth. Is é an próiseas fliuch ná an t-ábhar cumaisc a mheilt isteach sa sciodar le huisce, ansin brúigh agus scagaire chun díhiodráitiú isteach i gcíste láibe, agus an láib a fháisceadh isteach sa chuid láibe nó folamh láibe agus ansin sruthán.
Is é an modh leá leictreach ná an t-ábhar cumaisc a chur leis an bhfoirnéis stua, leá sa teocht ard atá déanta ag an stua, criostalú fionnuar, is féidir úsáid a bhaint as comhábhair nádúrtha amhábhar (cosúil le báicsít, etc.) a bhrú go díreach chuig<1.5mm particles without grinding, and then mixed with other powdered raw materials in the mixer.
Go ginearálta déantar sintéis mullite trí shintéiriú ag 1650 ~ 1700 céim. Is iad na príomhfhachtóirí a dhéanann difear do shintéis mullite trí shintéiriú ná íonacht amhábhar, míne amhábhar agus teocht calcination. Braitheann sintéis mullite trí mhodh shintéirithe go príomha ar Al? Ó? Críochnaítear an t-imoibriú céim soladach idir SiO2 agus sio2, agus mar sin cuirfidh feabhas ar scaipeadh na n-amhábhar dlús leis an bpróiseas imoibrithe céim soladach. Go háirithe, na cáithníní<8μm have a great effect on the formation and sintering of synthetic mullite. It can be seen that the full mixing and fine grinding of raw materials is an important process condition to promote the solid phase of the synthesis of mullite. Mullite generally begins to form at 1200 ° C and ends at 1650 ° C. At this time, it is microcrystalline, and the crystallization develops well when the temperature exceeds 1700℃. It can be seen that the combustion temperature directly affects the formation and crystal development of mullite. Therefore, heating to a certain firing temperature and extending a certain holding time are necessary conditions for the synthesis of mullite. The purity of the raw materials used to synthesize mullite is very strict, and a small amount of impurities will reduce the content of mullite. In industrial production, it is inevitable to bring a variety of impurities, mainly Fe? O? TiO? , CaO, MgO, Na? O·K? O, the most harmful of which is Na? O, K? O, they inhibit the formation of mullite and lead to the production of a large number of silicon-rich glass phases, reducing mullite content. Fe? O? It will slow down the mullite process and increase the amount of glass phase. Be TiO? When a small amount of Ti ions exist, part of Ti ions enter the mullite lattice to form a solid solution, promoting the formation of mullite and crystal development and growth, when the TiO2 content is too high, it still acts as a flux.
Ullmhaítear mullite leictreamúite tríd an gcomhdhúil a leá i bhfoirnéis stua leictreach, agus déantar an mullite a fhuaraithe as an leá. Tá an próiseas criostalaithe cosúil le próiseas Al? Ó? -SiO? Tá próiseas criostalaithe léaráid chéim an chórais cosúil. Nuair a bheidh an Al? Ó? Nuair a bhíonn comhdhéanamh teoiriciúil mullite níos airde ná 71.8%, foirmítear barrachas tuaslagtha Al. Ó? Is é an tuaslagán soladach de mullite, beta-mullite, ach Al? Ó? Níl an chuma ar an gcéim corundum ach ag 80%. Is é comhdhéanamh céim mianraí mullite comhleáite go ginearálta criostail mullite agus céim ghloine. Caighdeán tionscail mullite leáigh na Síne YB/T104-2004 "Electric melt mullite" an táirge mullite leá leictreach de réir Al? Ó? Tá an t-ábhar roinnte i ngráid DM-1 agus DM-2, agus tá na coinníollacha teicniúla ábhartha le feiceáil sna caighdeáin náisiúnta chomhfhreagracha. I gcomparáid le mullite sintéaraithe, tá criostail mullite comhleáite forbartha go maith le grán mór agus níos lú lochtanna, agus tá an méid criostail na céadta uair níos mó ná an mullite sintéaraithe, agus mar sin tá na hairíonna meicniúla teocht ard agus friotaíocht creimeadh sách maith.